Epoxy resin 128E is a bisphenol-A liquid epoxy resin modified with reactive diluent.
Автор: Hanepoxy
Загружено: 2025-04-12
Просмотров: 1113
This resin offers lower viscosity & lower
surface tension. Both these properties are advantageous while formulating. The low viscosity improves the cost effectiveness by
increasing filler loading & the low surface tension improves adhesion by better substrate wetting, it also helps in better pigment
wetting and thereby improve the pigment dispersion and stability.
Highly transparent and highly resistant to yellow 2:1 or 3:1 river glue
Features:environmentally friendly hard epoxy resin crystal AB adhesive can be room temperature or temperature curing, moderate viscosity, high transparency, self-foaming, self-leveling good, moderate operating time, suitable for manual and mechanical glue drops, curing high hardness, surface flat, high clear and high translucent, gloss, anti-yellowing (can be large volume of a potting 20kg)
Use process:
Ratio: A:B=2:1 and 3:1 optional.
Curing: 24 hours at room temperature, 48 hours demolding is recommended at room temperature, 72 hours can be sanded and polished!
Precautions:
1. The product to be potting needs to be kept dry and clean.
2. When using, please check the A agent first, observe whether there is any settlement, and mix the A agent well.
3. Take the amount according to the proportion, and weigh accurately, A, B agent mixing fully stirred to avoid incomplete curing.
4. Stir the hook in time for filling, and try to use up the mixed glue within the available time.
5. After filling, the glue will gradually penetrate into the crevices of the product. If necessary, please carry out the second ring, drip glue
6. During the curing process, please keep the environment clean so that impurities or dust will not fall into the surface of the uncured glue.